Paint Cork
Thermal finish paint in color, based on selected cork particles.
Description
Paint Cork was born out of a formulation, functional, and aesthetic challenge, developing a paint capable of combining the beauty and technology of a natural raw material such as cork, achieving an innovative balance between aesthetics and design.
Pintacork is characterized by providing total comfort in all seasons, allowing for a wide range of effects and maximum adaptation to all weather conditions. It can be used for colored finishes on walls and ceilings, both indoors and outdoors.
FEATURES OF SPRAY CORK
Performance
162 ft2 | 15m2 (2 layers)
Thickness
0,04 in | 1 mm
Finish
Textured
Colors
Color chart
Properties
– Contributes to insulation against cold and heat.
– Contributes to the hygrometric regulation of the environment, preventing mold and condensation dripping.
– Fire and high temperature resistant.
– Prevents thermal shock, dispersion, and overheating, contributing to energy savings.
– Excellent adhesion to surfaces such as metal, concrete, masonry, brick, plasterboard, fiber cement, and wood.
Uses
It can be used indoors or outdoors, on facades and EIFS systems, whether in new construction or renovation projects.
Preparation
Mix Spray Cork for at least 3 minutes or until a homogeneous mixture is achieved, then add dye, then mix for 3 more
minutes.
Application
It is applied mechanically using a texturing roller. The application must consist of two cross coats and provide a minimum thickness of 0.04 inches (1 mm).
Essays
ESSAYS
RESULTS
REGULATIONS
Water vapor transmisión test
36.8 (g/m2/24hr) | 5.29 (U.S. Perms)
ASTM E96 / E96M-22
Pull-out resistance
Metal/Stell 52.0 PSI | Stucco 9.2 PSI
ASTM D4541 – 17
Surface Burning Characteristics of Building Materials
Class ‘A’
ASTM E84-21
Fungus resistance
No fungal growths observed
ASTM G21-15
Thermal conductivity
0.050 ± 0.002 (W/m*k)
EN 12664:2001-1
Water vapor transmission properties
Permanence W 1,525E-09
(kg/m2 S Pa)
Resistivity rv 3,39 (MN s/g m)
Resistance Rv 0,008 (MN s/g)
Permeability Ᵹ 3,507E-12 (Kg/m s Pa)
Water vapor resistance factor μ 0,626
NCh 2457 of 2014
Thermal conductivity
0.041 (W/m*k)
NCh 850 of 2008
Adhesion direct traction method
Zinc 0,36 (Mpa) / Fiber cement 0,33 (Mpa)
NCh 2471 of 2000
Sound absorption coefficient
Sound reflective 0,13 < ɑ < 0,32
Range 400 Hz hasta 2000 Hz
ISO 10354-2